Sökning: "Termocykling"

Visar resultat 1 - 5 av 18 uppsatser innehållade ordet Termocykling.

  1. 1. Böjhållfasthet hos PMMA beroende på framställningsmetod, material och slitage efter termocykling. : -

    M1-uppsats, Malmö universitet/Odontologiska fakulteten (OD)

    Författare :Nemany Khadije; Abdallah Mohammed Awad; [2023]
    Nyckelord :Bettskenor; Böjhållfasthet; Fräsning; PMMA; TMD;

    Sammanfattning : Aim: The purpose of the study is to investigate the flexural strength of polymers (PMMA) intended for stabilization splints produced by heat-activated polymerization or milling, as well as how the flexural strength is affected wear.   Material and Methods: Twelve rectangular specimens in the dimensions 64 x 10 x 3 mm were produced by milling and divided into two groups: F (milled) and FS (milled subjected to wear testing). LÄS MER

  3. 2. Färgstabilitet hos protesbasmaterial beroende på framställningsteknik efter borstning, åldring, kaffeförvaring och rengöring.

    Kandidat-uppsats, Malmö universitet/Odontologiska fakulteten (OD)

    Författare :Ewa Chojnacka; Amanda Holmgren; [2023]
    Nyckelord :Färgstabilitet; polymerer; protesbasmaterial; spektrofotometer; termocykling.;

    Sammanfattning : Syfte: Syftet med föreliggande studie är att undersöka färgstabiliteten hos konventionellt varmpolymeriserat, fräst och 3D-printat material för protesbaser efter borstning, termocykling, kaffeförvaring och rengöring. Material och metod: Tio provkroppar av ett material per teknik framställdes; konventionell (ProBase Hot, Ivoclar), CAD/CAM subtraktiv (Ivotion Base, Ivoclar) och additiv teknik (Lucitone Digital Print, Dentsply). LÄS MER

  4. 3. Utmattning av implantat-förankrade bro-konstruktionermed ett frihängande led och två olika fixturdiametrar. En pilotstudie

    Kandidat-uppsats, Malmö universitet/Odontologiska fakulteten (OD)

    Författare :Ahmed Yassin; Mohammed Al-Haideri; [2023]
    Nyckelord :Cantilever; Dental implants; Fixed dental prosthesis; Fatigue; Fracture strength; Implant angulation; Brotthållfasthet; Dentala implantat; Fast protetik; Frihängande led; Implantatvinkling; Utmattning.;

    Sammanfattning : Purpose: The purpose of this study is to evaluate how implant-supported fixed dental prosthesis (FDP) restorations with a cantilever at abutment level resist fatigue by dynamic loading and thermocycling depending on the fixture diameters.   Material and method: The study involved two groups with three specimens in each group, based on the diameter of the fixture, 3. LÄS MER

  5. 4. Åldring av högtranslucent zirkoniumdioxid (3Y-TZP) i munmiljö jämfört med artificiella åldringsmetoder. En pilotstudie. : Aging of high translucent zirconium dioxide (3Y-TZP) in the oral environment compared to artificial aging methods. A pilot study.

    Kandidat-uppsats, Malmö universitet/Odontologiska fakulteten (OD)

    Författare :Emelie Tärnqvist; Ashraf Saadeh; [2022]
    Nyckelord :3Y-TZP; Artificiell åldring; Fasomvandling; In-vivo-åldring; Lågtemperatur-degradering;

    Sammanfattning : Sammanfattning Syfte Syftet med pilotstudien var att utvärdera hur kristallfaserna i högtranslucent zirkoniumdioxid (3Y-TZP) påverkas av åldring i munmiljö (in-vivo-metod) och in-vitro-metoder för artificiellt åldrande: vattenförvaring, termocykling och autoklavering. Material och metod Totalt framställdes 16 provkroppar av högtranslucent zirkoniumdioxid (3Y-TZP) med slutmått på 1 mm i tjocklek och 5 mm i diameter. LÄS MER

  7. 5. Brotthhållfastheten på monolitiska broar av flerskiktad zirkonia med olika konnektordimensioner och placering i en disk - En pilotstudie

    Kandidat-uppsats, Malmö universitet/Odontologiska fakulteten (OD)

    Författare :Iman Echreshavi; Linda Alsabti; [2022]
    Nyckelord :Connector dimension; Monolithic zirconia; Multi-layered zirconia; Yttria-stabilized zirconium dioxide; Y-TZP.;

    Sammanfattning : Purpose: The purpose of this study was to evaluate the fracture strength of monolithic FDPs of multi-layered zirconia (YML) with different connector dimensions and placement in the disc. Material and method: Forty 3-unit monolithic anterior FDPs were produced, 212223, and divided in four groups (n=10) based on the different connector dimensions and strategies for placement in KATANATM Zirconia Yttria Multi-Layered (YML)-disc. LÄS MER