Sökning: "adhesive surfaces"

Visar resultat 1 - 5 av 26 uppsatser innehållade orden adhesive surfaces.

  1. 1. Effect of temperature on early stage adhesion during TiAlN sliding against Inconel 718 and Stainless steel 316L : High temperature tribology

    Master-uppsats, Luleå tekniska universitet/Institutionen för teknikvetenskap och matematik

    Författare :Ahsan Ali; [2023]
    Nyckelord :High temperature tribology; Early-stage adhesion; Adhesive wear; Friction; Wear resistant coatings; Physical vapour deposition PVD coatings; TiAlN; Tungsten carbide WC Co ; Difficult to machine super alloys; Inconel 718; Stainless steel 316L; High-performance materials; Abrasion; Oxidation; Chipping; Ploughing; Characterization;

    Sammanfattning : High-performance materials such as stainless steels and nickel based super alloys are widely used in demanding applications where high mechanical and thermal properties are required. The applications of super alloys are mainly found in jet engines, power plants and gas turbines demanding high fatigue strength, corrosion and oxidation resistance as well as wear resistant properties. LÄS MER

  3. 2. Brandteknisk dimensionering av KL-trä – Jämförelse av nuvarande Eurokod 5 och kommande version

    Uppsats för yrkesexamina på grundnivå, Linnéuniversitetet/Institutionen för byggteknik (BY)

    Författare :Emil Karlsson; Gelan Hama Jan; [2023]
    Nyckelord :CLT; cross-laminated timber; fire safety; firedesign; Eurocode; KL-trä; korslimmat trä; brandsäkerhet; branddimensionering; Eurokod;

    Sammanfattning : Bygg- och fastighetssektorn är en bidragande faktor till växande koldioxidutsläpp och det krävs därför klimatbaserade innovationer för att arbeta mot ett hållbart och långsiktigt samhälle. På senare år har råvaran trä använts i form av KL-trä som konstruktionsmaterial i allt fler och större byggnader. LÄS MER

  4. 3. Evaluation of Refined Tribological Properties of Diamond Coated Cutting Tools Used in Machining of High-Strength Aluminum Alloys : Master thesis report regarding refined frictional & wear behavior of uncoated & CVD diamond coated WC-Co cemented carbide cutting tools used for machining of Al 7xxx alloys.

    Master-uppsats, Karlstads universitet/Fakulteten för hälsa, natur- och teknikvetenskap (from 2013)

    Författare :Christian Hultman; [2022]
    Nyckelord :tribology; machining; metal cutting; turning; milling; friction; wear; material transfer; surface technology; tribologi; skärande bearbetning; svarvning; fräsning; friktion; förslitning; nötning; materialöverföring; ytteknologi;

    Sammanfattning : High strength aluminum alloys have for a long time been a popular material utilized in the automotive and aerospace sector due to coveted mechanical properties in terms of weight, strength, fatigue, and corrosion. However, tribological mechanisms such as tribo-film formation and material transfer during the metal cutting manufacturing process of aluminum impose significant reduction of machining and tool-life performance. LÄS MER

  5. 4. Development of a Method to Predict the Adhesion of Industrial Paint Coating

    Master-uppsats, KTH/Fiber- och polymerteknologi

    Författare :Akheen Sadik; [2022]
    Nyckelord :Contact angle technique; optical tensiometer; paint coating; adhesion promoter; silane; kontaktvinkel; optisk tensiometer; ytbehandling; adhesion; silan;

    Sammanfattning : I samarbete med Sherwin-Williams AB, utvecklades en metod med kontaktvinkelmätning för att teoretiskt uppskatta vätbarhet och vidhäftningsförmåga av industriella färger på stålsubstrat. Optisk tensiometer och Youngs ekvation kombinerat med OWRK beräkningsmodell användes för att bestämma ytenergier. LÄS MER

  7. 5. Bindningsstyrka mellan komposit och porslin för metallkeramik med förbehandling av olika  reparationssystem

    Kandidat-uppsats, Malmö universitet/Odontologiska fakulteten (OD)

    Författare :Linnea Liljenborg; Ghinwah Chaaban; [2021]
    Nyckelord :Adhesive resin; bonding strength; composite material; metal-ceramics; porcelain repair system; Adhesiv resin; bindningsstyrka; kompositmaterial; metallkeramik; reparationssystem.;

    Sammanfattning : Syfte: Syftet med föreliggande in-vitro studie är att undersöka olika kompositbaserade reparationssystem och dess bindningsstyrka till porslin för metallkeramiska konstruktioner. Material och metod: Metallstavar tillverkades via CAD/CAM i CoCr (5.0x5.0x15. LÄS MER