Sökning: "steel melt"

Visar resultat 1 - 5 av 33 uppsatser innehållade orden steel melt.

  1. 1. Residual Products in the Steel Industry Used for Briquetting

    Kandidat-uppsats, KTH/Materialvetenskap

    Författare :Alexander Eriksson; Linn Isaksson; Jacob Lilliebjörn; [2023]
    Nyckelord :;

    Sammanfattning : This report looks at the implementation of briquetting in the Swedish steel industry. Briquetting is a process in which residual products are mixed and compressed into a brick-like body in order to be added to the melt in a furnace. This report investigates the type of materials commonly used in briquetting as of today. LÄS MER

  3. 2. Investigation of new hot melt adhesives with plasticisers based on renewable resources : Investigating the use of sustainable plasticisers in hot melt adhesives

    Kandidat-uppsats, Karlstads universitet/Institutionen för ingenjörs- och kemivetenskaper (from 2013)

    Författare :Shadi Feyzabi; [2023]
    Nyckelord :Hot melt adhesives; renewable; mineral oil; vegetable oil; rheology; viscosity; loop tack; adhesive strength; Smältlim; förnybar; mineralolja; vegetabilisk olja; reologi; viskositet; loop tack; vidhäftningsstyrka;

    Sammanfattning : Hot melt adhesives (HMA) are a class of adhesives that, unlike solvent-or waterborne counterparts, do not contain organic solvents or other carriers, and are produced and subsequently applied in a molten state. The main components of HMA are polymers, tackifying resins, and a plasticiser. LÄS MER

  4. 3. Apparent density for water atomized low-carbon steel powder

    Master-uppsats, KTH/Materialvetenskap

    Författare :Simon Lindström; [2023]
    Nyckelord :;

    Sammanfattning : Carbon content does not affect the apparent density for water atomized iron powder monotonically. At low carbon content, around 0.1 wt %, apparent density is higher than a similar powder with 0.3 wt % carbon. LÄS MER

  5. 4. Macrosegregation Prediction in Continuously Cast Steel Slabs

    Master-uppsats, Luleå tekniska universitet/Institutionen för teknikvetenskap och matematik

    Författare :Malek Al-Ameri; [2022]
    Nyckelord :;

    Sammanfattning : A prediction model [3] of macrosegregation in continuously cast steel slabs developed by Barber et al from Corus Teesside Technology Centre, UK as an extension of the work of Miyazawa and Schwerdtfeger [4] is presented in this thesis. Improvements have been made in the model to include the effect of many bulges between the supporting rolls induced by the ferrostatic pressure exerted on the solidifying shell by the liquid phase, which were approximated following a deflection of an elastic beam model. LÄS MER

  7. 5. Dissolution of Cored Wire in Steel Melt : Optimization of Feeding Rate

    Master-uppsats, KTH/Materialvetenskap

    Författare :Hagen Christian Hagens; [2022]
    Nyckelord :Cored wire injection · light alloy addition · feed rate optimization · inclusions modification · finite difference method;

    Sammanfattning : Calcium treatment is an established operation in the production of steels. Most importantly, it serves to modify detrimental inclusions in the melt for improved castability and superior product properties. Due to calcium’s low melting point and high vapour pressure, its addition to liquid steel is challenging and yields are generally low. LÄS MER