Metalization of Micro Fibrillated Cellulose (MFC) films

Sammanfattning: In this thesis, two MFC based films Carboxymethylated-Microfibrillated Cellulose (MFC) and Enzymatic-MFC were characterized and metalized in order to improve the barrier properties at high relative humidity. Several methods were used for the characterization process, which were Atomic Force Microscopy (AFM), Contact Angle (CA), Energy Dispersive Spectra (EDS), Light Microscopy (LM), Scanning Electron Microscopy (SEM), and Oxygen Transmission Rate (OTR). Physical Vapor Deposition (PVD) system was used for the metalization of film, a thin layer of aluminium with a thickness of 200 nm was deposited on the films. The results revealed that ENZ-MFC exhibit a higher roughness and lower OTR values, compared to CM-MFC. The contact angle values proved that both non-metalized MFC films exhibited a hydrophilic surface with values around 50 degrees. SEM and EDS images showed that both films exhibited surface defects with dimensions in the order of a micrometer. The best barrier improvement by metalization was achieved for the metalized CM-MFC, where the OTR values were decreased by one order of magnitude after metalization. However, for ENZ-MFC metalization did not improve OTR at high RH. The protective layer was successfully protecting the MFC film as long as the surface roughness of the film was not too high. The limit is between 40 and 140nm (in root mean square roughness values).