Phased Array Ultrasonic Testing of Austenitic Stainless Steel Welds of the 11 T HL-LHC Dipole Magnets

Sammanfattning: A routine non-destructive test method based on Phased Array Ultrasonic Testing (PAUT) has been developed and applied for the inspection of the first 11 T dipole prototype magnet half shell welds, and the test results are compared with the radiography and visual inspection results of the same welds. A manual scanner and alignment system have been developed and built to facilitate the inspection of the 5.5 m long welds, and to assure reproducibility of the PAUT results. Through the comparison of distance readings and signal amplitude for different focus lengths, a focal law with focus at 25 mm sound path has been selected for the routine inspection of the 15 mm thick austenitic stainless steel 11 T dipole welds. The defocusing properties (beam spread) due to the cylindrical geometry of the half shells and the sound path distance to the area of interest were taken into account. Dedicated sensitivity calibration weld samples with artificial defects (side-drilled-holes) have been designed and produced from 11 T dipole prototype austenitic stainless steel half shell welds. These provide representative calibration for the strongly attenuating and scattering austenitic stainless steel weld material. One scan with two phased array probes aligned parallel to the weld in 2 mm distance from the weld cap edge, and one scan with the probes aligned parallel to the weld in 12 mm distance from the weld cap edge are sufficient to show if the inspected welds fulfil the requirements of weld quality level B according to ISO 5817. The standard test duration for the two scans of the two 5.5 m long horizontal welds of the 11 T dipole magnets is about one day, provided that no defects are found that need to be characterized in more detail.