Aluminium alloys ability to catalyse the oxidation of biodiesel : Development of a procedure to test alloys

Sammanfattning: Biodiesel is a renewable and biodegradable fuel that has the possibility to replace conventional diesel fuel and reduce the environmental pollution. Despite its environmental benefits, it has been shown to cause damage to the vehicle engines, due to its oxidative properties. Different metals, such as copper, zinc and aluminium are present in the vehicle fuel system and have been shown to catalyse the oxidation of biodiesel. Several studies have been performed to investigate the interaction between these metals and fuel. However, some reports concluded contradicting results when it comes to the oxidation of biodiesel in contact with aluminium alloys. This project aimed therefore to investigate and create a simple method for comparing the catalytic effect on oxidation for metals, and use this method to evaluate the degradation rate of biodiesel in contact with aluminium alloys. Different heating methods and coating materials were tested using the biodiesel RME to develop the testing procedure. When a test procedure was established, three filter houses made from cast aluminium alloy and three aluminium ingots with different amount of copper were immersed in RME and the stability was evaluated. The results showed that using an oven at 80 °C to investigate the stability provided the most repeatable results, and the spray paint Auto K billack spray Universal appeared to be compatible to use with RME. The inner untreated surface of the fuel filter houses did not seem to increase the oxidation rate of biodiesel. Aluminium alloys with higher copper content degraded RME more than aluminium alloys with little/no copper, if the surface had been treated mechanically, but not to a large extent. This concludes that aluminium alloys may reduce the stability of biodiesel if it contains much copper and if the surface of the alloy has been treated. However, the detected reduction on oxidation stability could depend on other factors, and therefore it is recommended to conduct further experiments on test the aluminium alloys.