Thermal Stability of Arc Evaporated ZrCrAlN

Sammanfattning: This research explores the thermal stability of ZrCrAlN material system. For this purpose fourteen different compositions of ZrCrAlN coatings were deposited onto tungsten carbide substrates by using reactive cathodic arc evaporation. These compositions were further annealed at 800oC, 900oC, 1000oC and 1100oC temperatures. EDS was employed to specify the compositions. The crystal structure of the coatings were analysed by XRD, and the hardness of these coatings was determined by Nanoindentation. The experimental findings reported a significant age hardening of Zr0.16Cr0.12Al0.72N and a delayed h-AlN formation in Zr0.07Cr0.40Al0.52N. ZrCrAlN was thus proved to be thermally stable.