Effect of iron redox state on crystallization behaviour of Fayalite slags

Sammanfattning: In the copper smelting processes, the viscosity of the matte and the slag is an important factor for establishing efficiency. Impurities in the concentrates affect the viscosity not only by changing the melt structure but also by promoting precipitation of solid phase which sharply rises it. In this master thesis, a comprehensive methodology was established to study the MgO effects on the properties of a copper smelting slag. Thus, glassy samples were obtained and after confirmation of the composition and the glassy structure with EDS, SEM, and XRD analysis, they were examined through Ramanspectroscopy to study their glassy structure. Moreover, Mössbauer spectroscopy was used to determine the amount of Fe3+ in the samples. Models from the literature were compared to the experimental data. Coherence with the literature was found with the effect of MgO as a network modifier of the oxide melt structure and a promoter of high coordinated structures. Estimations through models were performed to study the iron redox equilibria of the melt and were compared with experimental data, but it was not possible to find the limit of Fe3+ at which precipitation of solid phase initiates.