Sökning: "Gleeble"

Visar resultat 1 - 5 av 6 uppsatser innehållade ordet Gleeble.

  1. 1. The Effect of Temperature Gradients During Intercritical Annealing of Advanced High Strength Steels : Method Development for Experimental Streamlining

    Master-uppsats, KTH/Materialvetenskap

    Författare :Helena Ek Jendrny; [2023]
    Nyckelord :AHSS; Gleeble; Intercritical annealing; Retained austenite; Medium Mn Steel; AHSS; Gleeble; interkritisk glödgning; austenit; Medium Mn stål;

    Sammanfattning : The third-generation advanced high strength steels, AHSS, represent an opportunity for today’s steel development, where lighter materials with maintained strength and toughness are in demand. The unique properties of these materials often stem from a tailored microstructure. LÄS MER

  3. 2. Styrning av svalningsförlopp vid släckglödgning av SAF2507

    Master-uppsats, KTH/Materialvetenskap

    Författare :Tim Juréen; [2023]
    Nyckelord :;

    Sammanfattning : Duplexa stål är en typ av rostfria stål vars mikrostruktur består av två olika faser till lika andel, som används för att de har en mycket bra kombination av korrosionsmotstånd och mekaniska egenskaper. En viktig process vid tillverkning av duplexa stål är släckglödgning, där stålet värms och sedan snabbkyls kontrollerat för att erhålla önskade mekaniska och korrosions-beständiga egenskaper. LÄS MER

  4. 3. Analysis of hot workability in 316L steel using ductile fracture criterions

    Uppsats för yrkesexamina på avancerad nivå, Luleå tekniska universitet/Institutionen för teknikvetenskap och matematik

    Författare :Viktor Strid; [2022]
    Nyckelord :Ductile fracture criterion; Finite Element Method; Hot working; 316L Stainless Steel; Fracture Modeling; Gleeble; Hot deformation;

    Sammanfattning : The focus of this thesis is to develop a simulation model for predicting ductile fractures during hot working at Alleima. The main fracture mechanism in these conditions is ductile fracture by void coalescence. The ductile fractures are caused by the linking of voids that appear when there is large plastic deformation near second-phase particles. LÄS MER

  5. 4. Microstructural characterization of quench annealed duplex SAF 2507 utilizing EBSD

    Uppsats för yrkesexamina på avancerad nivå, Uppsala universitet/Tillämpad materialvetenskap

    Författare :Simon Beyermann; [2022]
    Nyckelord :sigma phase; chi phase; electron backscatter diffraction; super duplex stainless steel; recrystallization; SAF 2507 UNS S32750 .;

    Sammanfattning : Producing large bars of duplex stainless steel free from precipitated embrittling phases isdifficult due to the many factors that influence precipitation. Research shows that intermetallicslike sigma and chi deteriorate principal material properties for the main application areas. LÄS MER

  7. 5. Characterization of Heat Treated LMwD Ti-6Al-4V to Study the Effect of Cooling Rate on Microstructure and Mechanical Properties

    Uppsats för yrkesexamina på avancerad nivå, Luleå tekniska universitet/Institutionen för teknikvetenskap och matematik

    Författare :Emil Edin; [2019]
    Nyckelord :Ti-6Al-4V; LMwD; Characterization; Alpha Laths;

    Sammanfattning : In this work, the influence of different cooling rates (5, 20, 50 and 100 °C/s) on the microstructure and mechanical properties of Laser Metal Wire Deposited (LMwD) Ti-6Al-4V was investigated, this was done using a thermal-mechanical physical simulation system (Gleeble 3800, DSI). Two different soak times above β transus (held at 1100 °C), 5 and 40 s, were used and after cooling to 150 °C, the samples were tensile tested. LÄS MER