Graphene Based Aqueous Ammonium Dual-Ion Batteries

Sammanfattning: The global transition to renewable energy sources is placing high demands on the development of effective energy storage methods, the most prevalent being batteries. Dual-ion batteries are a new battery technology that takes advantage of the simultaneous intercalation of both cations and anions. Dual-ion batteries can be made from environmentally friendly materials such as organic compounds or conductive polymers that are made up of highly abundant elements. These often have a lower cell voltage than metal-based batteries, allowing water-based electrolytes to be used without decomposing. This master’s thesis presents the synthesis, and electrochemical testing of a nanofibrous polyaniline cathode. It also presents the synthesis and electrochemical testing of two anodes being and graphene-enhanced polyimide, and perylene tetracarboxylic diimide (PTCDI). Aqueous ammonium sulfate of 1 M or 3 M concentration is used as electrolyte. A novel full-cell dual-ion battery is also constructed using polyaniline and PTCDI as electrodes. The addition of graphene to polyimide results in changes in morphology with decreased pore size and increased surface area for supposed improved reaction kinetics with the electrolyte. The electrochemical testing of this anode is however not successful. The polyaniline cathode has an early charge/discharge capacity of 184.5/85.2 mAh/g that decreases to 40.4/45.8 mAh/g after 100 cycles. The PTCDI anode has an early charge/discharge capacity of 80.2/87.3 mAh/g but cannot be evaluated after a few cycles due to electrolyte decomposition. For this reason, the electrolyte dependence on ammonium sulfate concentration is also investigated. An increase in molarity from 1 M to 3 M leads to increased stability of the electrolyte. The polyaniline//PTCDI full-cell has a voltage of 1.2 V and shows an early charge/discharge capacity of 17.6/11.9 mAh/g that decreases to 9.1/7.2 mAh/g after 100 cycles where the efficiency stabilizes at 80%.