Böjhållfastheten hos flerskiktade zirkoniamaterial beroende på sintringsprogram
Sammanfattning: Aim: The aim of the present study was to evaluate how the material KATANA ™ Zirconia YML is affected in strength depending on two different sintering programs. The evaluation of the strength was made by means of a biaxial flexural strength test. Material and method: A total of 48 test specimens, 32 specimens were produced by KATANA ™ Zirconia YML and 16 specimen cups that formed the control group, by KATANA ™. Zirconia UTML. The specimens were designed as circular disks and were placed in two different layers in the disk, between Enamel-Body 1 and Body 2-Body 3. The specimens were divided into two subgroups of which 24 specimens were quickly sintered and the remaining (n = 24) specimens were conventionally sintered and the strength was evaluated with a biaxial flexural strength test. Results: The highest mean value for the biaxial flexural strength test was shown by the test group which was high-speed sintered, with placement in Body 2 - Body 3. This was significant in comparison with other groups (p> 0.001) in addition to conventional sintered with the same placement in the disk. Both control groups showed low mean values in comparison with the test groups, control group K (414 MPa) as the lowest in comparison with all other groups. When comparing the two control groups S and K, no significant difference was shown. Conclusion: The bending strength varies depending on which layers are loaded regardless of fast and conventional sintering. The sintering parameters are significant for the bending strength.
HÄR KAN DU HÄMTA UPPSATSEN I FULLTEXT. (följ länken till nästa sida)