1. Investigation of Ductility Dip at 1000˚C in Alloy 617
Kandidat-uppsats, KTH/MaterialvetenskapSammanfattning : Alloy 617 displays a ductility dip during straining at exactly 1000˚C, leading to brittle fracture. A sudden decrease in ductility appearing during Gleeble hot ductility tests of Ni-based superalloys is a well-known phenomenon, while its cause is unknown. LÄS MER