  1. 1. Reprocessing and Characterization of Polybenzimidazole for High-Temperature Polymer Electrolyte Membrane Fuel Cells

    Master-uppsats, Lunds universitet/Centrum för analys och syntes

    Författare :Douglas Björkengren; [2023]
    Nyckelord :polymer electrolyte membrane fuel cells; PEMFC; HTPEMFC; polymer technology; polymer characterization; reprocessing; recycling; polybenzimidazole; PBI; Technology and Engineering;

    Sammanfattning : A reprocessing method of poly(2,2’-(m-phenylene)-5,5’-bibenzimidazole) (PBI) membranes recovered from the production line of High-Temperature Polymer Electrolyte Membrane Fuel Cells (HT-PEMFC) at Blue World Technologies (BWT) has been developed in order to reduce material loss in the production. Redissolution of scrap PBI membranes in poly(phosphoric acid) (PPA) and phosphoric acid (PA) was successful and the subsequent washing procedure produced PBI that could be redissolved in N,N-dimethyl acetamide (DMAc) and suitable for solution casting of new membranes. LÄS MER

  3. 2. Driftoptimering av luftningssystem och närsaltsdosering i ett skogsindustriellt reningsverk : Utvärdering av en biologisk reningsprocess ur ett energi-, miljö- och kostnadsperspektiv

    Master-uppsats, Karlstads universitet/Fakulteten för hälsa, natur- och teknikvetenskap (from 2013)

    Författare :Selma Zetterlund; Olivia Schwartz; [2023]
    Nyckelord :Simulink; reningsteknik; luftning; närsaltsdosering; reglerteknik;

    Sammanfattning : Dagens samhälle står inför många utmaningar där energieffektivisering är en stor del för att nå Sveriges energipolitiska mål. Det finns anledning att effektivisera och optimera energianvändningen i Sveriges papper- och massaindustrier då de står för en stor andel av nationell energiförbrukning. LÄS MER

  4. 3. Wet Spinning of Cellulose-Lignin Precursor for Carbon Fibers : Effect of Coagulation Bath Composition & Spin Finish

    Uppsats för yrkesexamina på avancerad nivå, Uppsala universitet/Tillämpad mekanik

    Författare :Julia Sundmark; [2023]
    Nyckelord :Carbon fiber; Cold alkali; Cold NaOH; lignin; cellulose; wet spinning; Kolfiber; kallalkali; lignin; cellulosa; våtspinning;

    Sammanfattning : Carbon fibers (CF) are a material with a composition of over 90% carbon, which has high mechanical properties and low density. This unique combination of properties makes it requirable in applications such as vehicles, aerospace, wind power, and space industries. Commercially made CF are made using the fossil raw material polyacrylonitrile (PAN). LÄS MER

  5. 4. Characterisation of Ionic Liquid doped Polybenzimidazole Membranes for Application in High-Temperature Proton Exchange Membrane Fuel Cells

    Master-uppsats, Lunds universitet/Kemiteknik (CI)

    Författare :Adam Jacobsson Trönndal; [2023]
    Nyckelord :Fuel cells; Phosphoric acid; Polybenzimidazole; PA-PBI; Ionic liquid; IL; High temperature proton exchange membrane fuel cell; HT-PEMFC; Electrochemical impedance spectroscopy; EIS; IL-PBI; Chemical engineering; Technology and Engineering;

    Sammanfattning : In this study four membranes were tested and evaluated against each other for use in high-temperature proton exchange membrane fuel cell (HT-PEMFC) applications. A phosphoric acid (PA) doped polybenzimidazole (PBI) membrane, was used as a reference as the current state-of-the-art. LÄS MER

  7. 5. Wet Spinning of Lignin and Cellulose Precursor Fibers Using Cold Sodium Hydroxide Dissolution

    Master-uppsats, KTH/Fiber- och polymerteknologi

    Författare :Nazariy Voytyuk; [2022]
    Nyckelord :Alkaline Dissolution; Cold Alkali Process; Lignin; Precursor Fibers; Wet spinning; Alkalisk upplösning; Kall alkaliprocess; Lignin; Prekursorfibrer; Våtspinning;

    Sammanfattning : Användningen av cellulosa och lignin för prekursorfibrer (PF) för kolfibrer (CF) är ett mycket intressant forskningsområde på grund av den stora miljöpåverkan som dagens PF-fossilbaserade råvara PAN har. Denna avhandling fokuserar på att utveckla PF med ett kallt NaOH-upplösningssystem med cellulosakoncentrationer från 4,5 till 5,5 viktprocent med varierande massaviskositet och tillsats av lignin från 0-40 viktprocent jämfört med cellulosa. LÄS MER