  1. 11. Mikrostruktur och tribologiska egenskaper för additivt tillverkat Inconel 718

    Uppsats för yrkesexamina på avancerad nivå, Uppsala universitet/Tillämpad materialvetenskap

    Författare :Jonas Larsson; [2016]
    Nyckelord :additive manufacturing; 3D-printing; tribology; superalloy; microstructure; anisotropy; wear; sliding contact; friction; hardness; additiv tillverkning; 3D-skrivning; tribologi; superlegering; Inconel 718; mikrostruktur; anisotropi; nötning; glidande kontakt; friktion; hårdhet;

    Sammanfattning : The present work was performed to improve the knowledge and understanding about the microstructure and tribological properties of additive manufactured Inconel 718 made with the technique Electron beam melting (EBM). The objective is to see if the microstructure and the properties have some anisotropy and if different processing routes differ. LÄS MER

  3. 12. Gradient formation in cemented carbides with 85Ni:15Fe-binder phase

    Uppsats för yrkesexamina på avancerad nivå, Uppsala universitet/Tillämpad materialvetenskap

    Författare :Niklas Larsson; [2015]
    Nyckelord :cemented carbide; alternative binderphase; sintering; gradient; hard metal;

    Sammanfattning : In today’s inserts used for metal cutting the binder phase consists of cobalt (Co).However, EU’s REACH programme and the U.S’s National Toxicity Programme(NTP) classified Co as toxic/carcinogenic. Therefore, there is a strong need toinvestigate alternative binder phases. LÄS MER

  4. 13. CFD analyses of the gas flow inside the vessel of a hot isostatic press

    Master-uppsats, KTH/Kraft- och värmeteknologi

    Författare :Andreas Åkerberg; [2012]
    Nyckelord :CFD; hot isostatic press; computational fluid dynamics; numerical methods; furnace; pressurized gas; vessel; rapid cooling;

    Sammanfattning : Hot isostatic pressing (HIP) is a thermal treatment method that is used to consolidate, densify or bondcomponents and materials. Argon gas is commonly used as the pressure medium and is isostaticallyapplied to the material with an excess pressure of 500-2000 bar and a temperature of 500-2200oC. LÄS MER

  5. 14. Effekten av lågtemperatursdegradering på Y-TZP som framställts med två olika processtekniker

    Kandidat-uppsats, Malmö högskola/Odontologiska fakulteten (OD)

    Författare :Ricardo Sakihama Laos; [2009]
    Nyckelord :lågtemperatursdegradering; Y-TZP HIP CIP;

    Sammanfattning : Det finns ett flertal fabrikanter som är inriktade på framställning av yttria-stabiliserad tetragonal polykristallin zirkoniumdioxid (Y-TZP), som är en oxidkeram som används inom dentalbranschen. Vid framställning av Y-TZP används huvudsakligen två pressningstekniker, kall isostatisk pressning (CIP) eller het isostatisk pressning (HIP). LÄS MER